| 大气等离子喷涂MoSi2-30Al2O3电热涂层的组织结构及性能 | |
| 引用本文： | 周炎哲,刘敏,杨焜,曾威,宋进兵,邓春明,邓畅光.大气等离子喷涂MoSi2-30Al2O3电热涂层的组织结构及性能[J].无机材料学报,2019,34(6):646-652. |
| 作者姓名： | 周炎哲 刘敏 杨焜 曾威 宋进兵 邓春明 邓畅光 |
| 作者单位： | 中南大学 材料科学与工程学院, 长沙 410083 广东省新材料研究所, 现代材料表面工程技术国家工程实验室, 广东省现代表面工程技术重点实验室, 广州 510650 |
| 基金项目： | 广州市珠江科技新星专项(201710010130);广东省科学院实施创新驱动发展能力建设专项(2017GDASCX-0111);广东省科技厅省属科研机构改革创新稳定项目(2017A070701027);广东省科技项目(2014B070705007) |
| 摘 要： | 以MoSi2-30Al2O3混合粉末为原料, 利用大气等离子喷涂技术制备MoSi2-Al2O3体系电热涂层。采用XRD、SEM、通电测试、热重-差热分析等对涂层的相组成、组织形貌和热稳定性进行表征。结果表明：MoSi2-30Al2O3电热涂层体系组织均匀致密, 添加Al2O3能改善MoSi2的电阻率及低温抗氧化性; MoSi2-30Al2O3涂层电热性能优异, 在循环加热测试中, 能稳定地加热到320 ℃并长时间保温, 辊面温度分布均匀, 中部温差控制在25 ℃之内; 循环加热过程中的氧化及热应力的弛豫会导致涂层产生裂纹及孔隙进而导致涂层电阻率升高。 |
| 关 键 词： | 电热材料 MoSi2-Al2O3复合涂层 等离子喷涂 电热性能 |
| 收稿时间： | 2018-09-03 |
| 修稿时间： | 2018-10-31 |
Microstructure and Property of MoSi2-30Al2O3 Electrothermal Coating Prepared by Atmospheric Plasma Spraying |
|
| Yan-Zhe ZHOU,Min LIU,Kun YANG,Wei ZENG,Jin-Bing SONG,Chun-Ming DENG,Chang-Guang DENG.Microstructure and Property of MoSi2-30Al2O3 Electrothermal Coating Prepared by Atmospheric Plasma Spraying[J].Journal of Inorganic Materials,2019,34(6):646-652. | |
| Authors: | Yan-Zhe ZHOU Min LIU Kun YANG Wei ZENG Jin-Bing SONG Chun-Ming DENG Chang-Guang DENG |
| Affiliation: | School of Materials Science and Engineering, Central South University, Changsha 410083, China The Key Lab of Guangdong for Modern Surface Engineering Technology, National Engineering Laboratory for Modern Materials Surface Engineering Technology, Guangdong Institute of New Materials, Guangzhou 510650, China |
| Abstract: | With MoSi2-30Al2O3 mixed powders as the raw material, MoSi2-30Al2O3 electrothermal coating was sprayed by atmospheric plasma spraying technology. The phase composition, microstructure and thermal stability of the coating were systematically studied by XRD, SEM, electrical test and differential thermal gravity analysis. The results show that MoSi2-30Al2O3 electrothermal coating shows dense microstructure. Al2O3 can improve the electrical resistivity and oxidation resistance of MoSi2 materials in low temperature. The coating exhibits an excellent electrical-heating performance. In the heating cycle test, it could be heated to 320 ℃ stably and exhibit uniform thermal distribution in the surface area. The temperature variation in roll’s central area can be controlled within 25 ℃; Oxidation and thermal stress relaxation during heating cycle would generate cracks and pores in the coating which would increase electrical resistivity. |
| Keywords: | electrothermal material MoSi2-Al2O3 composite coating atmospheric plasma spraying electrical- heating performance |