Recrystallization/precipitation behaviour in microalloyed steels

Microalloyed high-strength low-alloy (HSLA) steels contain additions of Nb, V, Ti, or in combination, in amounts of 0.01 to 0.1 weight percent to improve mechanical properties, which are strongly dependent on the thermomechanical interaction taking place in the course of rolling mill processes. The recrystallizatian of hat-twisted austenite has been investigated in a cylindrical specimen (f 6×50 mm) machined from hat rolled plates of 0,052 wt % Niobium microalloyed steel. Continuous and interrupted torsion test were carried out in the temperature range 1123 K to 1173 K after a solution treatment of 1.5 minutes at 1423 K and torque-twist data were analysed. The various methods were discussed for obtaining results from torsion tests. The effect of precipitation kinetics was appreciated by way of connection t_p/t_p(red), where t_p is the experimental measured time for the peak stress and t_p(red) is the newly defined reduced time. The softening ratio X and time t_0.05R for start of static recrystallization were established.

The correlation between precipitation and recrystallization is presented as a graphs for chosen requirements (temperature of austenitization, carbon and niobium content and strain rate). If temperature goes below 850°C, the restoration processes are hardly suppressed, both are limited by diffusion and Nb(CN) precipitation, which are extended dynamically in the range of strains rates 10^?2 to 1 s^?1.

In the present paper, an attempt is made to derive the PRTT diagram and to define all mathematical equations for describing recrystallization times t_0.05R, t_0.5R, t_0.95R and t_0.05P for the start of precipitation. In real metal forming processes such as the hot rolling of plates or strips the knowledge of these parameters and results is extremely important for the the correct microstructure and sheet quality to be obtained.