Properties of thin LPCVD silicon oxynitride films

Thin, uniform silicon oxynitride films with films thicknesses of ≤ 10 nm were successfully deposited by low pressure chemical vapor deposition (LPCVD). The reactant gases were SiH₂Cl₂, N₂O, and NH₃. The compositional uniformity of these films as a function of depth was good. The structure of these oxynitride films was found to be dominated by the mixed matrix of Si, N, and 0, rather than a physical mixture of SiO₂ and Si₃N₄ clusters. N-H bonding was observed and the total amount of hydrogen in the as-deposited film was on the order of 5 x l0²⁰/cm³. No H-OH or Si-OH bonds were detected. Excellent dielectric breakdown distributions were found for oxynitride films with equivalent oxide film thicknesses as low as 7.5 nm. The conduction of Si-N-0 films depended on film composition. A small capacitor-voltage (C-V) window (< 0.1 V) was observed for the Si-N-O/Si structures. The midgap surface state density was on the order of 5 x 10¹⁰/cm² /eV. Either trapping of holes or the generation of positive states were found after high field stressing of the oxynitride films.