| 对延长锌浸出渣挥发窑寿命的探讨 |
| |
| 引用本文： | 刘斯嘉,李向民,刘金良.对延长锌浸出渣挥发窑寿命的探讨[J].有色矿冶,2007,23(4):40-42,45. |
| |
| 作者姓名： | 刘斯嘉 李向民 刘金良 |
| |
| 作者单位： | 葫芦岛有色金属集团有限公司,辽宁,葫芦岛,125003 |
| |
| 摘 要： | 介绍了电解锌浸出渣在挥发窑处理过程中对窑使用寿命的影响因素及延长挥发窑寿命的探讨,着重介绍了耐火材料对挥发窑寿命的影响,根据生产实践情况来看,铝镁铬耐火砖在挥发窑上的应用效果最好,并取得很好的经济效益。
|
| 关 键 词： | 浸出渣 挥发窑 磨损 腐蚀 剥落 铝镁铬耐火砖 |
| 文章编号： | 1007-967X（2007）04-0040-04 |
| 修稿时间： | 2007-03-25 |
The Discussion of Extend the Service Life of Zinc Leaching Residue Volatility Kiln |
| |
| LIU Si-jia,LI Xiang-min,LIU Ji-liang.The Discussion of Extend the Service Life of Zinc Leaching Residue Volatility Kiln[J].Non-Ferrous Mining and Metallurgy,2007,23(4):40-42,45. |
| |
| Authors: | LIU Si-jia LI Xiang-min LIU Ji-liang |
| |
| Affiliation: | Huludao Nonferrous Metals Group Co. Ltd., Liaoning Huludao 125003, China |
| |
| Abstract: | The effecting factors of electrolytic Zinc leaching residue to the Kiln's service life during the processing of Volatility kiln were introduced.And the refractory`s effect was emphasized.The way of extending the service life of volatility kiln was also discussed.According to the practice of production,alumina magnesia-chrome fire brick on the volatility was the best and more economic benefit could be achieved. |
| |
| Keywords: | leaching residue volatility kiln wear corrosion spalling alumina magnesia-chrome fire brick |
| 本文献已被 CNKI 维普 万方数据 等数据库收录！ |