Influence of accelerated ageing on methacrylate‐based denture resins heterogeneity as viewed by ESR‐spin‐probe method

The electron‐spin‐resonance (ESR) spin‐probe method, was used to study the heterogeneity of denture resins based on poly(methyl methacrylate). Results for three resins processed by microwave energy, conventional curing and cold curing (depending on the curing procedure and exposed to ageing in various environmental conditions) were compared. All three cured resins were stored over the same time (1200 h) in distilled water at ambient temperature and in artificial saliva at 348 K. The temperature‐dependent ESR spectra of a spin probe dispersed in the denture resins are analyzed in terms of line‐shapes and line‐widths. The appearance of two spectral components was taken as an indication of resin heterogeneity. The results reveal that the cold‐cured resin has a lower local density in comparison with microwave and conventionally cured resin. The amount of residual monomer also contributes to the local motion of polymer segments. The change of denture resins exposed to ageing is influenced both by the structure of the original resin and the ageing conditions. Restricted motion of a spin probe incorporated into the acrylic resins exposed to accelerated ageing suggests additional crosslinking of polymer chains. The differences are observed for all the investigated resins, but the highest change is observed with the cold‐cured resin. The ESR results are accompanied by T_g and T_m measurements. Copyright © 2005 Society of Chemical Industry