Plasma etching of high-k and metal gate materials |
| |
Authors: | Keisuke Nakamura Kazushi Osari |
| |
Affiliation: | Department of Aeronautics and Astronautics, Graduate School of Engineering, Kyoto University, Yoshida-Honmachi, Sakyo-ku, Kyoto 606-8501, Japan |
| |
Abstract: | Etching characteristics of high-k dielectric materials (HfO2) and metal electrode materials (Pt, TaN) have been studied in high-density chlorine-containing plasmas at pressures around 10 mTorr. The etching of HfO2 was performed in BCl3 without rf biasing, giving an etch rate of about 5 nm/min with a high selectivity of >10 over Si and SiO2. The etching of Pt and TaN was performed in Ar/O2 with high rf biasing and in Ar/Cl2 with low rf biasing, respectively, giving a Pt etch rate of about several tens nm/min and a TaN etch rate of about 200 nm/min with a high selectivity of >8 over HfO2 and SiO2. The etched profiles were outwardly tapered for Pt, owing to the redeposition of etch or sputter products on feature sidewalls, while the TaN profiles were almost anisotropic, probably owing to the ion-enhanced etching that occurred. |
| |
Keywords: | Plasma etching Chlorine-containing plasma High-k dielectrics Metal electrode materials HfO2 Pt TaN |
本文献已被 ScienceDirect 等数据库收录! |
|