Improvement of Thermoelectric Power Factor of Hydrothermally Prepared Bi0.5Sb1.5Te3 Compared with its Solvothermally Prepared Counterpart

We report on the successful hydrothermal synthesis of Bi_0.5Sb_1.5Te₃, using water as the solvent. The products of the hydrothermally prepared Bi_0.5Sb_1.5Te₃ were hexagonal platelets with edges of 200–1500 nm and thicknesses of 30–50 nm. Both the Seebeck coefficient and electrical conductivity of the hydrothermally prepared Bi_0.5Sb_1.5Te₃ were larger than those of the solvothermally prepared counterpart. Hall measurements of Bi_0.5Sb_1.5Te₃ at room temperature indicated that the charge carrier was p-type, with a carrier concentration of 9.47 × 10¹⁸ cm⁻³ and 1.42 × 10¹⁹ cm⁻³ for the hydrothermally prepared Bi_0.5Sb_1.5Te₃ and solvothermally prepared sample, respectively. The thermoelectric power factor at 290 K was 10.4 μW/cm K² and 2.9 μW/cm K² for the hydrothermally prepared Bi_0.5Sb_1.5Te₃ and solvothermally prepared sample, respectively.