Gradient HfB2-SiC multilayer oxidation resistant coating for C/C composites |
| |
Authors: | Peipei Wang Mingde Tong Hanhui Wang Hejun Li Yujun Jia Bo Li Yulei Zhang Zhigang Zhao |
| |
Affiliation: | State Key Laboratory of Solidification Processing, Carbon/Carbon Composites Research Center, Northwestern Polytechnical University, Xi’an, Shaanxi 710072, PR China |
| |
Abstract: | The gradient HfB2 modified SiC coating was prepared on the surface of SiC-coated C/C composites by in-situ synthesis. Anti-oxidation behaviors of the coated C/C samples at 1773, 1873 and 1973?K were investigated. The results show that the gradient HfB2 modified SiC coatings possess excellent oxidation resistance, which can protect C/C substrates from oxidation for 800, 305 and 100?h at 1773, 1873 and 1973?K, respectively. In addition, with the oxidation temperature increasing, the evaporation of the Hf-Si-O glass layer and the active oxidation of SiC were accelerated, which is the reason for the worst oxidation resistance of the sample at 1973?K among the three temperatures. |
| |
Keywords: | Carbon/carbon composites Coating Oxidation |
本文献已被 ScienceDirect 等数据库收录! |
|