Untersuchungen zum Korrosionsverhalten von AlLi-Legierungen
Authors:R. Holbein  A. Dembeck
Abstract:
Corrosion behaviour of aluminium-lithium alloys The AlLiMgCu alloy 8090 was studied in its texturated fine grained version “A” and in its recrystallized coarse grain structured version “C” in different artificially aged conditions in reference to several other AlLi alloys, each in its heat treatment condition of practical interest, and to the convetional alloy 2024 T3. The subject of research was the general corrosion behaviour of semifinished AlLi products, particularly sheet material, under alternate and permanent immersion conditions in neutral 3.5% sodium chloride solution; the stress corrosion behaviour was studied under constant load in the long transverse direction according to ASTM G44 and G49. The underaged conditions, which are the relevant conditions for technical application of the 8090 “A” and “C” sheets, showed an approximately equivalent or even better corrosion behaviour in comparison to the lithium-free alloy 2024 T3 in the corrosion tests with unloaded specimens. The threshold above which the AlLi alloy 8090 in some heat treatment conditions is attacked by stress corrosion cracking within the 30 days lasting constant load test depends on alloy composition, testing direction, grain size, stretch-forming, artificial ageing condition, surface pretreatment and the specimens' dimensions.
Keywords:
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号