High-strength ZrB2-based ceramics prepared by reactive pulsed electric current sintering of ZrB2–ZrH2 powders

Fully densified ZrB₂-based ceramic composites were produced by reactive pulsed electric current sintering (PECS) of ZrB₂–ZrH₂ powders within a total thermal cycle time of only 35 min. The composition of the final composite was directly influenced by the initial ZrH₂ content in the starting powder batch. With increasing ZrH₂ content, ZrB₂–ZrO₂, ZrB₂–ZrB–ZrO₂ and ZrB₂–ZrB–Zr₃O composites were obtained. The ZrB₂–ZrB–ZrO₂ composite derived from a 9.8 wt% ZrH₂ starting powder exhibited an excellent flexural strength of 1382 MPa combined with a Vickers hardness of 17.1 GPa and a fracture toughness of 5.0 MPa m^1/2. The high strength was attributed to a fine grain size and the removal of B₂O₃ through reaction with Zr. Higher ZrH₂ content starting powders were densified through solution-reprecipitation resulting in the formation of coarser angular ZrB₂–ZrB composites with a Zr₃O grain boundary phase with a fracture toughness of 5.0 MPa m^1/2 and an acceptable strength in the 852–939 MPa range.