碳纤维增强树脂复合材料-热成型钢超混杂层合板层间力学性能

通过双悬臂梁试验(DCB)研究了金属表面处理和界面插层协同作用对碳纤维增强树脂复合材料(CFRP)-热成型钢超混杂层合板层间力学性能的影响。试验结果表明，采用金属表面处理与界面插层协同增韧方案，可以极大地提升层合板的I型层间断裂韧性。其中，喷砂/界面胶膜插层试件(GB36#/AF)的I型层间断裂韧性相比于脱脂试件提高了343%；喷砂/界面纯树脂插层试件(GB36#/EP)相比于脱脂试件，其Ⅰ型层间断裂韧性提高了129%。并基于内聚区模型对CFRP-热成型钢超混杂层合板分层失效进行了有限元模拟。最后借助激光共聚焦扫描显微镜(LSM)、接触角测量仪(CAG)、扫描电子显微镜(SEM)等对热成型钢表面形貌和试件的断裂面进行了表征并揭示了层间增韧的机制。 

Interlaminar mechanical properties of carbon fiber reinforced plastics-thermoformed steel super-hybrid laminates

The synergistic effects of the metal surface treatments and interleaves on the interlaminar mechanical properties of the carbon fiber reinforced plastics (CFRP) composite-thermoformed steel super-hybrid laminates were investigated. Double cantilever beam tests (DCB) show that the Mode-I interlaminar fracture toughness of the laminates can be greatly improved by combining metal surface treatment and inserting interleaf. Among them, the interlaminar Mode-I fracture toughness of the specimens with sandblasting/adhesive film interleaves (GB36#/AF) and sandblasting/epoxy resin interleaves (GB36#/EP) increase by 343% and 129% compared with that of the degreased specimens respectively. In addition, based on the cohesive zone model, the delamination of the CFRP-thermoformed steel super-hybrid laminates was analyzed by finite element method. Finally, to uncover the toughing mechanism, confocal laser scanning microscopy (LSM), contact angle goniometer (CAG) and scanning electron microscopy (SEM) were employed to characterize the surface morphology of the thermoformed steel and the fracture surface of the tested laminates.