Effects of micro-alloying and production process on precipitation behaviors and mechanical properties of HRB600 |
| |
Authors: | Meng-jiao Zhang Hui-ting Wang Chang-sheng Xie Zhan Guo |
| |
Affiliation: | 1. School of Metallurgical Engineering, Anhui University of Technology, Ma′anshan 243002, Anhui, China;2. Technology Center, Ma′anshan Iron & Steel Company Limited, Ma′anshan 243000, Anhui, China |
| |
Abstract: | Effects of micro-alloying elements and production process on microstructure, mechanical properties and precipitates of 600 MPa grade rebars were studied by using pilot test, metallographic observa-tion, tensile test, thermodynamic calculation and transmission electron microscopy.The results show that the tested steels are composed of ferrite and pearlite, in which the content range of pearlite is 33%-45%.For vanadium micro-alloyed steel, interphase precipitation strengthening effect of V can be promoted and the yield strength of tested steels can be increased with increasing V content and de-creasing finishing rolling temperature.The temperature of terminated cooling should be more than 700℃ when the water cooling is used.When niobium is added to the steel, more coarse (Nb,V)C,N precipitates are generated at high temperature, so that the solid solubility of precipitated phases of vanadium is reduced and the precipitation strengthening effect of vanadium is weakened. |
| |
Keywords: | Micro-alloying High-strength steel rebar Thermo-mechanical controlling process Mechanical property Precipitation strengthening Thermodynamics |
本文献已被 CNKI 万方数据 等数据库收录! |
|