Effect of composition and milling parameters on the critical ball milling of Ti–Si–B powders

The absence of brittle phases and elevated temperature during ball milling of a powder mixture containing a large amount of ductile component can contribute to reach an excessive agglomeration denoting a critical ball milling (CBM) behavior. This work reports in the effect of composition and milling parameters on the CBM behavior of Ti–Si–B powders. High-purity elemental Ti–Si–B powder mixtures were processed in a planetary ball mill in order to prepare the Ti₆Si₂B compound and two-phase Ti + Ti₆Si₂B alloys. TiH₂ chips instead of titanium powder were used as a starting material. To avoid elevated temperature in the vials during ball milling of Ti–Si–B powders the process was interrupted after each 10 min followed by air-cooling. Following, the milled powders were hot-pressed at 900 °C for 1 h. Samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy dispersive spectrometry (EDS). Short milling times followed by air-cooling contributed to obtain a large amount of powders higher than 75% in the vials. Only Ti and TiH₂ peaks were observed in XRD patterns of Ti–Si–B and TiH₂–Si–B, respectively, suggesting that extended solid solutions were achieved. The large amount of Ti₆Si₂B and Ti + Ti₆Si₂B structures were formed during hot pressing from the mechanically alloyed Ti–Si–B and TiH₂–Si–B powders.