Tensile Strength of Yttria-Stabilized Tetragonal Zirconia Polycrystals

Tensile strengths of 2.0 to 5.0 mol% Y₂O₃-stabilized ZrO₂ polycrystals were described using the newly developed tensile testing method. The tensile test was conducted by attaching three strain gauges on both sides of a rectangular bar that was 10 mm by 1 mm by 200 mm. The tensile strength of tetragonal ZrO₂ polycrystals (TZP) containing 2.0 mol% Y₂O₃ showed 745 MPa, whereas the bend strength of this material was 1630 MPa. Inelastic behavior of the stress-strain curve was observed at critical stresses and strains of 500 to 700 MPa and 0.25% to 0.35%, respectively. Although deviation from proportionality was observed to be small, it increased with the increase of temperature from −100° to 200°C.