固溶处理对热轧Inconel 601合金组织与力学性能的影响

通过光学显微镜、扫描电镜、万能拉伸试验机和硬度计等研究了 1 080～1 200℃固溶温度对热轧态Inconel 601合金微观组织和力学性能的影响.结果表明:热轧态合金基体为沿轧制方向拉长的奥氏体晶粒组织,同时弥散有少量氮化物,沿晶界有大量碳化物析出.随着固溶温度的升高,再结晶晶粒逐渐长大,碳化物缓慢溶解,强度及硬度...

Effect of Solution Treatment on Structure and MechanicalProperties of Hot Rolled Inconel 601 Alloy

Effect of 1 080 ~ 1 200 ℃ solution temperature on structure and mechanical properties of hat rolled Inconel 601 alloy is studied by means of optical microscope, scanning electron microscopy, hardness tester and tensile tester. The results show that the structure of the hot rolled alloy matrix is elongated austenite grain structure with less dispersed nitride, but the massive carbide precipitated along austenite grain boundary. With the increasing solution temperature, the recrystallization grain size increases gradually, the carbide dissolves slowly, the strength and hardness decrease gradually. When the solution temperature is 1 160 ℃，the crystal grain size is uniform, the carbide dissolves completely, the HRB hardness value of alloy decreases from 84 to 71, and the elongation increases from 52% to 70%. The best mechanical properties of alloy can be obtained by solid solution treated process at 1 140 ~ 1 160 ℃ for 50 min.