The ternary system: silicon–titanium–uranium

Phase equilibria in the system Si–Ti–U were established at 1000 °C by optical microscopy, EMPA and X-ray diffraction. Two ternary compounds were observed and were characterised by X-ray powder data refinement: (1) stoichiometric U₂Ti₃Si₄ (U₂Mo₃Si₄-type) with a small homogeneity region of about 3 at.% exchange U/Ti and (2) U_2−xTi_3+xSi₄ (Zr₅Si₄-type) extending at 1000 °C for 0.7<x<1.3. Mutual solubility of U-silicides and Ti-silicides was found to be below about 1 at.%. The Ti,U-rich part of the diagram was also investigated at 850 °C establishing the tie-lines to the low temperature compounds U₂Ti and U₃Si. U₂Ti₃Si₄ is weakly paramagnetic following a Curie–Weiss law above 50 K with μ_eff.=2.67 μ_B/U, Θ_P=−150 K and χ₀=1.45×10⁻³ emu/mol (18.2×10⁻⁹ m³/mol).