Influence of the Y2O3 Content and Temperature on the Mechanical Properties of Melt-Grown Al2O3–ZrO2 Eutectics

The effect of Y₂O₃ content on the flexure strength of melt-grown Al₂O₃–ZrO₂ eutectics was studied in a temperature range of 25°–1427°C. The processing conditions were carefully controlled to obtain a constant microstructure independent of Y₂O₃ content. The rod microstructure was made up of alternating bands of fine and coarse dispersions of irregular ZrO₂ platelets oriented along the growth axis and embedded in the continuous Al₂O₃ matrix. The highest flexure strength at ambient temperature was found in the material with 3 mol% Y₂O₃ in relation to ZrO₂(Y₂O₃). Higher Y₂O₃ content did not substantially modify the mechanical response; however, materials with 0.5 mol% presented a significant degradation in the flexure strength because of the presence of large defects. They were nucleated at the Al₂O₃–ZrO₂ interface during the martensitic transformation of ZrO₂ on cooling and propagated into the Al₂O₃ matrix driven by the tensile residual stresses generated by the transformation. The material with 3 mol% Y₂O₃ retained 80% of the flexure strength at 1427°C, whereas the mechanical properties of the eutectic with 0.5 mol% Y₂O₃ dropped rapidly with temperature as a result of extensive microcracking.