Correlating phase and microstructure development versus dielectric properties in La and Er co-doped Bi4Ti3O12 ferroelectric ceramics

Bi_3.25La_0.75−xEr_xTi₃O₁₂ and Bi_3.25La_0.75Ti_3−xEr_xO_12−δ ceramics were prepared and studied in this work in terms of dopant-induced phase and microstructure development as well as dielectric response. The results show that introduction of Er³⁺ tends to reduce the materials’ sintering temperature and average grain size. Moreover, it was noted that in these systems the substitution site of this dopant is controlled by valence state and ionic radii mismatch effects. In particular, even when a nominal substitution of Ti⁴⁺ is conceived, here it is found that Er³⁺ also incorporates at the (Bi,La)³⁺ sites. These and other interesting concluding remarks from this work, including Er³⁺ tolerance, were possible only after comparing, especially, the X-ray diffraction results and the intrinsic ferroelectric characteristics extracted from the dielectric measurements.