| Ca2SiO3Cl2∶Dy3+单一基质白光荧光粉的制备及发光特性 |
| |
| 引用本文： | 宁青菊,王邦卿,郭芳芳,乔畅君,王秀峰.Ca2SiO3Cl2∶Dy3+单一基质白光荧光粉的制备及发光特性[J].功能材料,2012,43(9):1126-1129. |
| |
| 作者姓名： | 宁青菊 王邦卿 郭芳芳 乔畅君 王秀峰 |
| |
| 作者单位： | 陕西科技大学材料科学与工程学院,陕西西安,710021 |
| |
| 基金项目： | 国家自然科学基金资助项目，陕西省教育厅专项科研计划资助项目，陕西科技大学博士基金资助项目，陕西科技大学研究生创新基金对本项目的大力资助致谢:感谢陕西科技大学研究生创新基金对本项目的大力资助! |
| |
| 摘 要： | 采用溶胶-凝胶法合成了发射白光的Ca2SiO3Cl2∶Dy3+荧光粉。利用XRD分析了荧光粉的晶体结构,其为四方晶系。在350nm近紫外光激发下,荧光粉呈白光发射,有两个主发射峰位分别于482和573nm,分别对应于Dy3+的4F9/2→6H15/2和4F9/2→6H13/2跃迁;监测573nm最强发射峰,激发光谱覆盖200～450nm,主激发峰位于350nm。研究结果表明保温时间的延长有利于发射强度的提高,伴随着Dy3+浓度的增大,发射光谱图中的两个主发射峰先增强后减弱,Dy3+的最佳浓度为2%(摩尔分数)。
|
| 关 键 词： | 白光LED Ca2SiO3Cl2 Dy3+掺杂 发光 |
Preparation and luminance properties of the single white emitting phosphor Dy^3＋ doped Ca2SiO3Cl2 |
| |
| NING Qing-ju,WANG Bang-qing,GUO Fang-fang,QIAO Chang-jun,WANG Xiu-feng.Preparation and luminance properties of the single white emitting phosphor Dy^3＋ doped Ca2SiO3Cl2[J].Journal of Functional Materials,2012,43(9):1126-1129. |
| |
| Authors: | NING Qing-ju WANG Bang-qing GUO Fang-fang QIAO Chang-jun WANG Xiu-feng |
| |
| Affiliation: | (School of Materials Science and Engineering, Shaanxi University of Science and Technology,Xi’an 710021,China) |
| |
| Abstract: | Ca2SiO3Cl2∶Dy3+ white light phosphors was synthesized by sol-gel method.The phase of the samples was characterized by powder X-ray diffract ion(XRD),it has tetragonal system.The phosphor shows two major emission peaks locating at 482 and 573nm by the near ultraviolet excitation peak of 350nm,which correspond to the 4F9/2→6H15/2 and 4F9/2→6H13/2 characteristics transport of Dy3+,monitoring the strong emission peak at 573nm,the excitation band was covered from 300 to 470nm and the main peak of was located at 350 nm.The emission intensities increase with extending of the holding time.The experiment results suggested that the strongest emission was obtained when the concentration of the Dy3+ ions was 2mol%. |
| |
| Keywords: | white light emitting diode Ca2SiO3Cl2 : Dy^3+ doped luminescence |