| 数控弯曲下TA18高强钛管回弹对壁厚减薄和截面畸变的影响 |
| |
| 引用本文： | 王 艳,杨 合,李 恒,詹 梅,宋飞飞,李光俊,许旭东. 数控弯曲下TA18高强钛管回弹对壁厚减薄和截面畸变的影响[J]. 稀有金属材料与工程, 2012, 41(7): 1221-1225 |
| |
| 作者姓名： | 王 艳 杨 合 李 恒 詹 梅 宋飞飞 李光俊 许旭东 |
| |
| 作者单位： | 1. 西北工业大学 凝固技术国家重点实验室,陕西 西安,710072
2. 成都飞机T业(集团)有限公司,四川 成都,610092 |
| |
| 基金项目： | 凝固技术国家重点实验室自主研究课题 (0400-N8QT0219);材料成形与模具技术国家重点实验室开放课题研究基金 (09-10);西北工业大学基础研究基金（JC201028） |
| |
| 摘 要： | 通过ABAQUS有限元显/隐式方法模拟研究了不同芯棒和压块参数下回弹对TA18高强钛管壁厚减薄及截面畸变的影响。结果表明:在不同的工艺参数下TA18高强钛管卸载回弹后,壁厚减薄率与回弹前的相对差均小于10%;但截面畸变率与回弹前的相对差除极个别测量点外,均大于35%,甚至超过60%,且回弹后截面畸变率稳定变形区的"平台"现象消失。
|
| 关 键 词： | 回弹 TA18高强钛管 数控弯曲 壁厚减薄 截面畸变 |
| 收稿时间： | 2011-07-23 |
Effect of Springback on Wall Thinning and Section Distortion for High Strength TA18 Tube in NC Bending |
| |
| Wang Yan,Yang He,Li Heng,Zhan Mei,Song Feifei,Li Guangjun and Xu Xudong. Effect of Springback on Wall Thinning and Section Distortion for High Strength TA18 Tube in NC Bending[J]. Rare Metal Materials and Engineering, 2012, 41(7): 1221-1225 |
| |
| Authors: | Wang Yan Yang He Li Heng Zhan Mei Song Feifei Li Guangjun Xu Xudong |
| |
| Affiliation: | 1. State Key Laboratory of Solidification processing, Northwestern Polytechnical University, Xi’an 710072, China) (2. Chengdu Aircraft Industry (Group) Corporation Ltd., Chengdu 610092, China) |
| |
| Abstract: | The influence of the springback in high strength TA18 tubes on the wall thinning and section distortion under different process parameters was investigated using ABAQUS Explicit/Standard finite element models. The results show that the wall thinning ratios after unloading-springback are less than 10% under different process parameters for high strength TA18 tubes, while the section distortion ratios after springback are more than 35%, even 60% except a few measured points. The "platform" of section distortion ratio at stable forming zone disappears after springback. |
| |
| Keywords: | springback high strength TA18 tube NC bending wall thinning section distortion |