Effect of Ca Substitution on the Superconductivity of La2.5Y0.5CaBa3(Cu0.88Fe0.12)7Oz

The structural and superconducting properties of single-phase La_2.5–y Y_0.5Ca_1+y Ba₃ (Cu_0.88Fe_0.12)₇O _z (LYCaBCuFe) (y= 0.0–1.0) compounds with triple perovskite structure are investigated using X-ray diffraction, resistivity, a.c. susceptibility, and oxygen content measurements. Increasing Ca substitution for La resulted in a decrease in unit cell axes and volume. T _c ^R=0 shows a marginal increase from 31 K to 37 K for y = 0.0–0.21 and thereafter it decreases with increasing y leading to zero T _c ^R=0 at y 0.84. This shows that the suppression of T _c from 80 K to 31 K by Fe doping at x = 0.12 La_2.5Y_0.5CaBa₃(Cu_1–x Fe _x )₇O _z cannot be compensated by appropriate hole doping with Ca in LaYCaBCuFe.