Effect of the annealing conditions on the electrical characteristics of p+/n shallow junctions

Shallow p+/n junctions are produced by low-energy (10-keV) boron implantation into amorphous silicon layers formed by a prior implantation of Si+ ions. Junctions about 0.1 µm deep with good electrical characteristics (reverse current density Jr< 10^-7A/cm²at - 1 V) are obtained both by electron-beam annealing (1100°C, 2 s) and conventional furnace annealing (800°C, 30 min). It is shown that, in the case of the furnace treatment, lower annealing temperatures produce very high reverse currents, while excellent electrical characteristics (Jr< 10^-8A/cm²) are achieved at higher annealing temperatures (900°C), the junction extending, however, much deeper into silicon (0.26 µm).