Reinforcement of Hadfield steel matrix by oriented high‐chromium cast iron bars

To attain a wear‐resistant material compatible with high hardness and high toughness, Hadfield steel matrix was reinforced by oriented high chromium cast iron bars, through inserting high chromium alloys flux‐cored welding wires into Hadfield steel melt at 1500 ± 10 °C. The obtained composites were investigated by XRD, SEM, micro‐hardness, three‐body abrasion wear and impact toughness testers. The results show that the alloy powders inside the flux‐cored welding wires can be melted by the heat capacity of Hadfield steel melt and in situ solidified into high chromium cast iron bar reinforcements tightly embedded in the matrix. The micro‐hardness of reinforcements of the water‐quenched composite is about four times higher than that of the matrix. The impact toughness of the water‐quenched composite is higher than that of the as‐cast composite and lower than that of Hadfield steel, and its fracture mechanism is very complicated and refers to brittle and ductile mixture fracture mode. The excellent impact toughness and better wear resistance of the water‐quenched composite are attributed to combine fully the advantages and avoid the drawbacks of both Hadfield steel and high chromium cast iron. Additionally, in industrial application, the pulverizer plate produced by this composite, has also better wear resistance compared to the reference Hadfield steel pulverizer plate.