Investigation of the titanium–indium system

The phase diagram of the Ti–In system was determined using DTA, XRD and EDX analyses. The existence of the phases Ti₂In₅ Mn₂Hg₅ type structure, space group P4/mbm, a=0.99995(3), c=0.29960(2) nm] and Ti₃In Ni₃Sn type structure, space group P6₃/mmc, a=0.5978(1), c=0.4812(1) nm] was confirmed. The phase previously labeled Ti₃In₂ was found to exist in a narrow homogeneity region near Ti₅₆In₄₄. Rietveld refinement of the XRD powder pattern yielded solutions compatible with a Cu₃Au-type or a BiIn-type crystal structure, but not with a CuAu-type crystal structure. Furthermore, at 38.5 at.% In, a new phase was observed having a γ-brass related crystal structure Ti₈In₅, space group , a=0.99578(6) nm]. The intermetallic phases were formed by a cascade of peritectic reactions ending in a eutectic at >99 at.% indium between Ti₂In₅ and (In) at 0.4 K below the melting temperature of pure indium.