Evaluation of Y2O3 gate insulators for a-IGZO thin film transistors

In this work, Y₂O₃ was evaluated as a gate insulator for thin film transistors fabricated using an amorphous InGaZnO₄ (a-IGZO) active layer. The properties of Y₂O₃ were examined as a function of various processing parameters including plasma power, chamber gas conditions, and working pressure. The leakage current density for the Y₂O₃ film prepared under the optimum conditions was observed to be ~ 3.5 × 10^− 9 A/cm² at an electric field of 1 MV/cm. The RMS roughness of the Y₂O₃ film was improved from 1.6 nm to 0.8 nm by employing an ALD (Atomic Layer Deposition) HfO₂ underlayer. Using the optimized Y₂O₃ deposition conditions, thin film transistors (TFTs) were fabricated on a glass substrate. The important TFT device parameters of the on/off current ratio, sub-threshold swing, threshold voltage, and electric field mobility were measured to be 7.0 × 10⁷, 0.18 V/dec, 1.1 V, and 3.3 cm²/Vs, respectively. The stacked insulator consisting of Y₂O₃/HfO₂ was highly effective in enhancing the device properties.