Plasma-assisted CO2 reforming of methane over Ni-based catalysts: Promoting role of Ag and Sn secondary metals

Carbon dioxide (CO₂) and methane (CH₄) are the primary greenhouse gases (GHGs) that drive global climate change. CO₂ reforming of CH₄ or dry reforming of CH₄ (DRM) is used for the simultaneous conversion of CO₂ and CH₄ into syngas and higher hydrocarbons. In this study, DRM was investigated using Ag–Ni/Al₂O₃ packing and Sn–Ni/Al₂O₃ packing in a parallel plate dielectric barrier discharge (DBD) reactor. The performance of the DBD reactor was significantly enhanced when applying Ag–Ni/Al₂O₃ and Sn–Ni/Al₂O₃ due to the relatively high electrical conductivity of Ag and Sn as well as their anti-coke performances. Using Ag–Ni/Al₂O₃ consisting of 1.5 wt% Ag and 5 wt% Ni/Al₂O₃ as the catalyst in the DBD reactor, 19% CH₄ conversion, 21% CO₂ conversion, 60% H₂ selectivity, 81% CO selectivity, energy efficiency of 7.9% and 0.74% (by mole) coke formation were achieved. In addition, using Sn–Ni/Al₂O₃, consisting of 0.5 wt% Sn and 5 wt% Ni/Al₂O₃, 15% CH₄ conversion, 19% CO₂ conversion, 64% H₂ selectivity, 70% CO selectivity, energy efficiency of 6.0%, and 2.1% (by mole) coke formation were achieved. Sn enhanced the reactant conversions and energy efficiency, and resulted in a reduction in coke formation; these results are comparable to that achieved when using the noble metal Ag. The decrease in the formation of coke could be correlated to the increase in the CO selectivity of the catalyst. Good dispersion of the secondary metals on Ni was found to be an important factor for the observed increases in the catalyst surface area and catalytic activities. Furthermore, the stability of the catalytic reactions was investigated for 1800 min over the 0.5 wt% Ag-5 wt% Ni/Al₂O₃ and 0.5 wt% Sn-5 wt% Ni/Al₂O₃ catalysts. The results showed an increase in the reactant conversions with an increase in the reaction time.