| 11 t铸锭帽口绝热板和保护渣对H13钢成坯率的影响 |
| |
| 引用本文： | 宋书雅,赵俊学,杨薇,仇圣桃,李小明. 11 t铸锭帽口绝热板和保护渣对H13钢成坯率的影响[J]. 特殊钢, 2014, 35(2): 30-32 |
| |
| 作者姓名： | 宋书雅 赵俊学 杨薇 仇圣桃 李小明 |
| |
| 作者单位： | 1. 西安建筑科技大学冶金工程学院，西安 710055 ；2. 钢铁研究总院国家连铸中心，北京 100081； |
| |
| 摘 要： | 针对钢厂热作模具钢H13成坯率低的冶金质量问题,对影响成坯率的相关质量进行了统计分析,得出因帽口保温性能差所造成的疏松缺陷占不合格钢锭总量的58%~76%。通过将SiO2绝热板的体积密度和导热率分别由1.65 g/cm3和0.317 W/(m·K)降至0.87 g/cm3和0.21 W/(m·K),优化低碳复合保护渣的组成,使其熔点和粘度分别由原来的1258℃和1.8 Pa·s降至1147℃和0.9 Pa·s,使钢锭平均成坯率由原来的75%提高至80%。
|
| 关 键 词： | H13热作模具钢 铸锭帽口 绝热板 保护渣 成坯率 |
| 收稿时间： | 2013-09-05 |
Influence of 11 t Ingot Hot Top Insulating Board and Shield Flux on Billet Yield of Steel H13 |
| |
| Song Shuya,Zhao Junxue,Yang Wei,Qiu Shengtao,Li Xiaoming. Influence of 11 t Ingot Hot Top Insulating Board and Shield Flux on Billet Yield of Steel H13[J]. Special Steel, 2014, 35(2): 30-32 |
| |
| Authors: | Song Shuya Zhao Junxue Yang Wei Qiu Shengtao Li Xiaoming |
| |
| Affiliation: | 1.School of Metallurgical Engineering, Xi'an University of Architecture and Technology, Xi'an 710055 ；2.National Engineering Research Center of Continuous Casting Technology, Central Iron and Steel Research Institute, Beijing 100081; |
| |
| Abstract: | According to metallurgical quality issue about low billet yield of hot working die steel H13 at steel works, the statistic analysis on relative quality to influence on billet yield has been carried out to get that the porosity defects caused by poor insulation of hot top make up 58%-76% of the total non-qualified ingot. With decreasing the volume density and heat conductivity of SiO2 insulating board respectively from original 1.65 g/cm3 and 0.317 W/(m • K) to 0.87 g/cm3 and 0.21 W/( m • K) , and optimizing the ingredient of low carbon shield synthetic flux to decrease its melting point and viscosity respectively from original 1258 °C and 1.8 Pa • s to 1147 °C and 0.9 Pa • s, the average billet yield of ingot increases from original 75% to 80% . |
| |
| Keywords: | Hot Working Die Steel H13 Ingot Hot Top Insolating Board Shielding Flux Billet Yield |