The effects of microstructure,strength level,and crack propagation mode on stress corrosion cracking behavior of 4135 steel

The stress corrosion cracking (SCC) susceptibility of 4135 steel in a simulated sea water solution has been analyzed in an attempt to understand the effect that microstructural changes associated with the corresponding changes in strength level have on both intergranular (IG) and transgranular (TG) crack propagation modes. After a selection of heat treatments, the following different microstructural variables were studied: the effect of grain size on IG fracture processes; the influence of the grade of tempering on the SCC resistance and crack propagation mode; and the effect of type and content of bainite and the effect of ferrite in mixed microstructures. A global analysis shows that the typical SCC resistance-strength level inverse relationship can only be applied when the microstructure re-mains invariable. An important microstructural control of SCC behavior was found for TG processes at moderate and low strength levels. The data analysis showed the following: a beneficial effect of increasing the grain size when crack propagates at grain boundaries without precipitates; the existence of a critical tempering temperature so that a sudden IG-TG change happens without any apparent relation to microstructural changes; the beneficial effect of bainite presence as a substitute for mar-tensite and high SCC resistance of structures containing over 50 pct ferrite, associated with their low strength levels.