Properties of poly(ethylene terephthalate)/poly(ethylene naphthalate) blends

Blends composed of poly(ethylene terephthalate) (PET) as the majority component and poly(ethylene naphthalate)(PEN) as the minority component were melt-mixed in a single screw extruder at various PET/PEN compound ratios. Tensile and flexural test results reveal a good PET/PEN composition dependence, indicating that the compatibility of the blends is effective in a macrodomain. In thermal tests, single transitions for T_g, T_m and T_c (crystallization temperature), respectively, are observed from DSC as well as single T_g from DMA except for 50/50 blends. These results suggests that the compatibility is sufficient down to the submicron level. Moreover, isothermal DSC tests along with Avrami analysis indicate that PET's crystallization is significantly retarded when blended with PEN. Results in this study demonstrate that PEN is a highly promising additive to improve PET's spinnability at high speeds.