Sc Addition to (Bi,Pb)2Sr2Ca2Cu3Ox Freeze-Dried Ceramic

In a freeze-dried nitrate precursor powder with cation composition Bi:Pb:Sr:Ca:Cu = 1.7:0.3:2.0:2.5:3.5, Sc₂O₃ was added. The stoichiometry for the mixed precursor powder was Bi:Pb:Sr:Sc:Ca:Cu = 1.7:0.3:2.0:0.25:2.5:3.5. The two nitrate precursor powders with and without Sc were thermally decomposed, pressed, and sintered in the same conditions. They show different behavior, as revealed by thermal analysis, X-ray diffraction (XRD), Scanning electron microscopy (SEM), and χ′(T) measurements. Addition of Sc slows down synthesis processes, including 2223-phase during reactive sintering. After 70 h of sintering, 43% of 2223-phase formed in the pellet with Sc, whereas in the Sc-free pellet, 51% of the 2223-phase was attained. Moreover, addition of Sc leads to a certain morphology, resulting in lower superconducting characteristics.