Microstructures, densification and mechanical properties of TiC–Al2O3–Al composite by field-activated combustion synthesis

Dense TiC–Al₂O₃–Al composite was prepared with Al, C and TiO₂ powders by means of electric field-activated combustion synthesis and infiltration of the molten metal (here Al) into the synthesized TiC–Al₂O₃ ceramic. An external electric field can effectively improve the adiabatic combustion temperature of the reactive system and overcome the thermodynamic limitation of reaction with x < 10 mol. Thereby, it can induce a self-sustaining combustion synthesis process. During the formation of Al₂O₃–TiC–Al composite, Al is molten first, and reacted with TiO₂ to form Al₂O₃, followed by the formation of TiC through the reaction between the displaced Ti and C. Highly dense TiC–Al₂O₃–Al with relative density of up to 92.5% was directly fabricated with the application of a 14 mol excess Al content and a 25 V cm⁻¹ field strength, in which TiC and Al₂O₃ particles possess fine-structured sizes of 0.2–1.0 μm, with uniform distribution in metal Al. The hardness, bending strength and fracture toughness of the synthesized TiC–Al₂O₃–Al composite are 56.5 GPa, 531 MPa and 10.96 MPa m^1/2, respectively.