Thermal analysis of poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) irradiated under vacuum

Poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) (PHBV) was irradiated by ⁶⁰Co γ‐rays (doses of 50, 100 and 200 kGy) under vacuum. The thermal analysis of control and irradiated PHBV, under vacuum was carried out by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The tensile properties of control and irradiated PHBV were examined by using an Instron tensile testing machine. In the thermal degradation of control and irradiated PHBV, a one‐step weight loss was observed. The derivative thermogravimetric curves of control and irradiated PHBV confirmed only one weight‐loss step change. The onset degradation temperature (T_o) and the temperature of maximum weight‐loss rate (T_p) of control and irradiated PHBV were in line with the heating rate (°C min^?1). T_o and T_P of PHBV decreased with increasing radiation dose at the same heating rate. The DSC results showed that ⁶⁰Co γ‐radiation significantly affected the thermal properties of PHBV. With increasing radiation dose, the melting temperature (T_m) of PHBV shifted to a lower value, due to the decrease in crystal size. The tensile strength and fracture strain of the irradiated PHBV decreased, hence indicating an increased brittleness. Copyright © 2004 Society of Chemical Industry