Wet chemical synthesis of Gd+3 doped vanadium Oxide/MXene based mesoporous hierarchical architectures as advanced supercapacitor material

In this paper, Gd³⁺ doped V₂O₅/Ti₃C₂T_x MXene (GVO/MX) hierarchical architectures have been synthesized by wet chemical approach. As prepared GVO/MX composite, along undoped VO and unsupported GVO were well characterized by XRD, FESEM, EDX, FT-IR and BET techniques. Electrochemical performance of VO, GVO and GVO/MX was evaluated by CV, GCD and EIS measurements. Among the three electrodes, GVO/MX composite exhibited highest electrochemical activity with the optimum specific capacitance of 1024 Fg^-1 at 10 mVs^?1. The specific capacitance of GVO/MX was ～1.7 and ～3 times higher than unsupported GVO (585 Fg^-1) and VO (326 Fg^-1), respectively. The cyclic life of GVO/MX with capacitance retention 96.12% was observed at 60 mVs^?1. EIS measurements showed reduction in electrochemical impedance for GVO/MX as compared to GVO and VO. The corresponding impedance values of Rct and Resr for GVO/MX were calculated as 18 Ω and 1.8 Ω, respectively. The superior capacitive ability of GVO/MX can be ascribed to its unique morphology, short diffusion path and high surface area of fabricated composite. Considering it, the present work provides a feasible strategy to fabricate highly effective electrode materials for next generation energy storage devices.