Size dependence of THz region dielectric properties for barium titanate fine particles

Barium titanate (BaTiO₃) crystallites with various particle sizes from 22 to 500 nm were prepared by the two-step thermal decomposition method of barium titanyl oxalate. Various characterizations revealed that these particles were impurity-free, defect-free, dense BaTiO₃ particles. The powder dielectric measurement clarified that the dielectric constant of BaTiO₃ particles with a size of around 58 nm exhibited a maximum of over 15,000. To explain this size dependence, the THz region dielectric properties of BaTiO₃ fine particles, especially Slater mode frequency, were measured using the far infrared (FIR) reflection method. As the result, the lowest Slater mode frequency was obtained at 58 nm. This tendency was completely consistent with particle size dependence of the dielectric constant.