Positive Temperature Coefficient of Electrical Resistivity below 150 K in Barium Strontium Titanate

The resistivity of Ba_{(1– y )(1– x )}Sr _y (1– x )La _x TiO₃ceramics with x = 0.0025 and y = 0.25, 0.5, 0.75, and 0.9 was measured between 50 and 400 K. A resistivity anomaly corresponding to the positive temperature coefficient of electrical resistivity (PTCR) effect was observed for all compositions. The onset temperature decreased from 320 K ( y = 0.25) to 70 K ( y = 0.9). The extent of the PTCR effect was significantly enhanced for the strontium-rich composition and reached ∼8 orders of magnitude for y = 0.9. These results strongly suggested the possibility to fabricate PTCR devices based on (Sr,Ba)TiO₃ ceramics for application at cryogenic temperatures.