Role of vanadium ions,oxygen vacancies,and interstitial zinc in room temperature ferromagnetism on ZnO-V2O5 nanoparticles

In this work, we present the role of vanadium ions (V⁺⁵ and V⁺³), oxygen vacancies (V_O), and interstitial zinc (Zn_i) to the contribution of specific magnetization for a mixture of ZnO-V₂O₅ nanoparticles (NPs). Samples were obtained by mechanical milling of dry powders and ethanol-assisted milling for 1 h with a fixed atomic ratio V/Zn?=?5% at. For comparison, pure ZnO samples were also prepared. All samples exhibit a room temperature magnetization ranging from 1.18?×?10⁻³ to 3.5?×?10⁻³ emu/gr. Pure ZnO powders (1.34?×?10⁻³ emu/gr) milled with ethanol exhibit slight increase in magnetization attributed to formation of Zn_i, while dry milled ZnO powders exhibit a decrease of magnetization due to a reduction of V_O concentration. For the ZnO-V₂O₅ system, dry milled and thermally treated samples under reducing atmosphere exhibit a large paramagnetic component associated to the formation of V₂O₃ and secondary phases containing V⁺³ ions; at the same time, an increase of V_O is observed with an abrupt fall of magnetization to σ?~?0.7?×?10⁻³ emu/gr due to segregation of V oxides and formation of secondary phases. As mechanical milling is an aggressive synthesis method, high disorder is induced at the surface of the ZnO NPs, including V_O and Zn_i depending on the chemical environment. Thermal treatment restores partially structural order at the surface of the NPs, thus reducing the amount of Zn_i at the same time that V₂O₅ NPs segregate reducing the direct contact with the surface of ZnO NPs. Additional samples were milled for longer time up to 24 h to study the effect of milling on the magnetization; 1-h milled samples have the highest magnetizations. Structural characterization was carried out using X-ray diffraction and transmission electron microscopy. Identification of V_O and Zn_i was carried out with Raman spectra, and energy-dispersive X-ray spectroscopy was used to verify that V did not diffuse into ZnO NPs as well to quantify O/Zn ratios.