| 大体积混凝土温度裂缝产生机理和控制措施 |
| |
| 引用本文： | 张庆华.大体积混凝土温度裂缝产生机理和控制措施[J].山西建筑,2009,35(19):145-146. |
| |
| 作者姓名： | 张庆华 |
| |
| 作者单位： | 临沂市公路勘察设计院,山东,临沂,276000 |
| |
| 摘 要： | 通过分析大体积混凝土温度裂缝产生的原因，提出防止大体积混凝土温度裂缝产生的主要任务，从设计和施工两方面总结了大体积混凝土温度裂缝的控制措施，从而有效的解决大体积混凝土温度裂缝问题。
|
| 关 键 词： | 大体积混凝土 温度裂缝 控制措施 |
Analysis on production mechanism of temperature cracks in mass concrete and control measures |
| |
| ZHANG Qing-hua.Analysis on production mechanism of temperature cracks in mass concrete and control measures[J].Shanxi Architecture,2009,35(19):145-146. |
| |
| Authors: | ZHANG Qing-hua |
| |
| Affiliation: | ZHANG Qing-hua |
| |
| Abstract: | Through analysis on the reasons caused the temperature cracks produced in mass concrete major duties to prevent the production of temperature cracks in mass concrete are proposed,at the same time corresponding control measures are proposed from two aspects: design and construction,in order to effectively resolve temperature cracking problems of mass concrete. |
| |
| Keywords: | mass concrete temperature crack control measure |