| 混凝土中钢筋锈蚀原因与防锈蚀设计研究 | |
| 引用本文： | 王军. 混凝土中钢筋锈蚀原因与防锈蚀设计研究[J]. 混凝土, 2008, 0(8) |
| 作者姓名： | 王军 |
| 作者单位： | 山东理工大学,山东,淄博,255049;北京科技大学,北京,100083 |
| 摘 要： | 碳化和氯离子是引起混凝土结构中钢筋锈蚀的最主要原因,通过分析碳化的发生机理和影响因素及混凝土中氯离子的来源和诱发钢筋锈蚀的机理,论述氯离子在混凝土中扩散的Fick定律和提高混凝土结构耐久性的措施. |
| 关 键 词： | 碳化 氯离子 钢筋锈蚀 耐久性栽 |
Reasons of steel corrosion and corrosion-resistance design in concrete |
|
| WANG Jun. Reasons of steel corrosion and corrosion-resistance design in concrete[J]. Concrete, 2008, 0(8) | |
| Authors: | WANG Jun |
| Affiliation: | WANG Jun1,2(1.Sh,ong University of Technology,Zibo 255049,China,2.University of Science , Technology Beijing,Beijing 100083,China) |
| Abstract: | Carbonation and chloride are the most important reasons which caused steel corrosion in concrete structure.The mechanism of carbonation occurrence and effect was analyzed.The chloride source in concrete and corrosion mechanism were introduced.The Fick model which proposed the chloride diffusion in concrete was stated.Measures improving concrete structure durability were offered. |
| Keywords: | carbonation chloride steel corrosion durability |