Untersuchungen zur Spannungsrißkorrosionsbeständigkeit nichtrostender Stähle mit unterschiedlichem Verformungsgrad

Investigations on stress corrosion cracking resistivity of stainless steels with different degree of cold straining Within the context of the elaboration of a new approval for stainless steels for civil engineering applications the question arised whether cold straining could adversely affect the resistance against stress corrosion cracking. By means of experimental tests with different stainless steels it should be clarified whether cold straining increase the stress corrosion cracking susceptibility under high chloride loads like e.g. in swimming hall atmospheres. The investigations were carried out using the high-alloyed steels 1.4462 and 1.4529. As reference material with known susceptibility against stress corrosion cracking the steel 1.4301 was used. The tests were performed using U-bent and tension specimens with saturated MgCl₂ salt spots. Indications for an increase in stress corrosion cracking susceptibility of the cold drawn steel were not found.