Intermetallic reactions in a Sn-20In-2.8Ag solder ball-grid-array package with Au/Ni/Cu pads

The intermetallic compounds formed during the reflow and aging of Sn-20In-2.8Ag ball-grid-array (BGA) packages are investigated. After reflow, a large number of cubic-shaped AuIn₂ intermetallics accompanied by Ag₂In precipitates appear in the solder matrix, while a Ni(Sn_0.72Ni_0.28)₂ intermetallic layer is formed at the solder/pad interface. With further aging at 100°C, many voids can be observed in the solder matrix and at the solder/pad interface. The continuous distribution of voids at the interface of specimens after prolonged aging at 100°C causes their bonding strength to decrease from 5.03 N (as reflowed) to about 3.50 N. Aging at 150°C induces many column-shaped (Cu_0.74Ni_0.26)₆(Sn_0.92In_0.08)₅ intermetallic compounds to grow rapidly and expand from the solder/pad interface into the solder matrix. The high microhardness of these intermetallic columns causes the bonding strength of the Sn-20In-2.8Ag BGA solder joints to increase to 5.68 N after aging at 150°C for 500 h.