| Cu46Zr46Al8非晶合金电子束焊接特性分析 |
| |
| 引用本文： | 王廷,石志远,李宁,宋凯凯,冯吉才. Cu46Zr46Al8非晶合金电子束焊接特性分析[J]. 焊接学报, 2018, 39(8): 38-41. DOI: 10.12073/j.hjxb.2018390197 |
| |
| 作者姓名： | 王廷 石志远 李宁 宋凯凯 冯吉才 |
| |
| 作者单位： | 1. 哈尔滨工业大学(威海) 先进焊接与连接国家重点实验室, 威海 264209;2. 哈尔滨工业大学(威海) 山东省特种焊接技术重点实验室, 威海 264209;3. 山东大学(威海) 机电与信息工程学院, 威海 264209 |
| |
| 基金项目： | 国家自然科学基金资助项目（U1637104）；山东省重点研发计划项目（2017GGX30110） |
| |
| 摘 要： | 对Cu46Zr46Al8非晶合金进行了电子束焊接，并分析了接头微观组织转变、显微硬度分布及拉伸性能.结果表明，Cu46Zr46Al8非晶合金电子束焊接接头熔化区组织大部分仍为非晶态，过冷液相区内发生晶化形成Cu-Zr金属间化合物.焊接接头熔化区与母材硬度相当，过冷液相区硬度值显著降低.接头抗拉强度及韧性相比母材都明显降低，拉伸断裂于过冷液相区内的脆性化合物层，呈现典型的沿晶脆性断裂特征.
|
| 关 键 词： | 电子束焊接 非晶合金 微观组织 力学性能 |
| 收稿时间： | 2017-11-03 |
Characteristic of electron beam welded Cu46Zr46Al8 BMGs |
| |
| WANG Ting,SHI Zhiyuan,LI Ning,SONG Kaikai,FENG Jicai. Characteristic of electron beam welded Cu46Zr46Al8 BMGs[J]. Transactions of The China Welding Institution, 2018, 39(8): 38-41. DOI: 10.12073/j.hjxb.2018390197 |
| |
| Authors: | WANG Ting SHI Zhiyuan LI Ning SONG Kaikai FENG Jicai |
| |
| Affiliation: | 1. Shandong Provincial Key Laboratory of Special Welding Technology, Harbin Institute of Technology at Weihai, Weihai 264209, China;2. State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China;3. School of Mechanical, Electrical & Information Engineering, Shandong University at Weihai, Weihai 264209, China |
| |
| Abstract: | Cu46Zr46Al8 BMGs have been joined by the electron beam welding (EBW) technique. The microstructural transformation, microhardness profile across the welded joint and the tensile property have been analyzed in this paper. The results showed that major microstructure in fusion zone remained amorphous state. Crystallization occurred in the supercooling liquid zone (SLZ) and a large amount of Cu-Zr intermetallics were produced. The microhardness in fusion zone was similar to the base metal and microhardness of supercooling liquid zone was significantly reduced. The tensile strength and toughness of the welded joint were lower than those of base metal. Fracture occurred in the brittle compounds layer of supercooling liquid zone with a typical brittle intergranular fracture mode. |
| |
| Keywords: | electron beam welding BMGs microstructure mechanical properties |