Effect of Ni/tubular g-C3N4 on hydrogen storage properties of MgH2

Additive doping is one of the effective methods to overcome the shortcomings of MgH₂ on the aspect of relatively high operating temperatures and slow desorption kinetics. In this paper, hollow g-C₃N₄ (TCN) tubes with a diameter of 2 μm are synthesized through the hydrothermal and high-temperature pyrolysis methods, and then nickel is chemically reduced onto TCN to form Ni/TCN composite at 278 K. Ni/TCN is then introduced into the MgH₂/Mg system by means of hydriding combustion and ball milling. The MgH₂–Ni/TCN composite starts to release hydrogen at 535 K, which is 116 K lower than the as-milled MgH₂ (651 K). The MgH₂–Ni/TCN composite absorbs 5.24 wt% H₂ within 3500 s at 423 K, and takes up 3.56 wt% H₂ within 3500 s, even at a temperature as low as 373 K. The apparent activation energy (E_a) of the MgH₂ decreases from 161.1 to 82.6 kJ/mol by the addition of Ni/TCN. Moreover, the MgH₂–Ni/TCN sample shows excellent cycle stability, with a dehydrogenation capacity retention rate of 98.0% after 10 cycles. The carbon material enhances sorption kinetics by dispersing and stabilizating MgH₂. Otherwise, the phase transformation between Mg₂NiH₄ and Mg₂NiH_0.3 accelerates the re/dehydrogenation reaction of the composite.