Enhanced hydrogen evolution reaction catalyzed by carbon-rich Mo4.8Si3C0.6/C/SiC nanocomposites via a PDC approach

In this study, mesoporous carbon-rich Mo_4.8Si₃C_0.6/C/SiC ceramic nanocomposites were successfully prepared via a single-source precursor route, starting from allylhydridopolycarbosilane (AHPCS, SMP-10), bis(acetylacetonato) dioxomolybdenum (VI) MoO₂(acac)₂], and divinylbenzene (DVB). Besides, polystyrene (PS) was used as a pore former. The obtained carbon-rich single-source precursor/PS mixtures were pyrolyzed at 1100°C, and then annealed at 1350°C-1600°C to fabricate a series of carbon-rich Mo_4.8Si₃C_0.6/C/SiC ceramics comprised of high carbon content above 50 wt%. In comparison to the carbon-poor materials, the carbon-rich samples retain the higher specific surface area up to 214.6-304 m²/g at higher annealing temperatures (1350°C-1600°C) due to the enhancement of carbothermal reaction. The carbon-rich samples synthesized at 1500°C, denoted as SM/Mo/PS/DVB 2-1-4-2 1500 exhibit enhanced electrocatalytic performance with ultra-low overpotentials of 119 mV vs reversible hydrogen electrode at a current density of 10 mA cm⁻² in acidic media, which is superior to that of the Mo_4.8Si₃C_0.6/C/SiC ceramic (138 mV) with lower carbon content reported in our previous study. Therefore, our porous materials comprised of high carbon content and Nowotny phase (Mo_4.8Si₃C_0.6, NP) are considered as promising catalysts for the hydrogen evolution reaction (HER).