| Abstract: | Because of its high–temperature chemical stability, SiC ceramic is a promising material for high-temperature device applications such as thermoelectric energy converters. However, the electrical conductivity of SiC ceramic is too low for it to be used as a thermoelectric energy converter at the cold junction. Therefore, we propose a SiC-Si functionally gradient material (FGM) in order to improve the electrical conductivity of the SiC ceramic at the cold junction. An SiC rod was fired in a temperature gradient furnace. One end of the SiC rod was maintained at 2473 K and the other end was maintained at 1973 K for 30 min. After firing, the porous SiC edge fired at 1973 K was dipped into molten Si in order to infiltrate molten Si into the porous SiC. The microstructure of the FGM is classified into three regions: the SiC-Si composite material; the porous SiC ceramic; and the densified SiC ceramic. The electrical conductivity, the Seebeck coefficient and the thermal conductivity for each region of SiC-Si FGM was measured at 300 K; a figure of merit was calculated. The figure of merit of the SiC-Si FGM at the cold junction, at room temperature, was 108 times higher than that of a nongradient SiC ceramic. |