Separation characteristics of tetrapropylammoniumbromide templating silica/alumina composite membrane in CO2/N2, CO2/H2 and CH4/H2 systems

Nanoporous silica membrane without any pinholes and cracks was synthesized by organic templating method. The tetrapropylammoniumbromide (TPABr)-templating silica sols were coated on tubular alumina composite support ( γ-Al₂O₃/ α-Al₂O₃ composite) by dip coating and then heat-treated at 550 °C. By using the prepared TPABr templating silica/alumina composite membrane, adsorption and membrane transport experiments were performed on the CO₂/N₂, CO₂/H₂ and CH₄/H₂ systems. Adsorption and permeation by using single gas and binary mixtures were measured in order to examine the transport mechanism in the membrane. In the single gas systems, adsorption characteristics on the α-Al₂O₃ support and nanoporous unsupport (TPABr templating SiO₂/ γ-Al₂O₃ composite layer without α-Al₂O₃ support) were investigated at 20–40 °C conditions and 0.0–1.0 atm pressure range. The experimental adsorption equilibrium was well fitted with Langmuir or/and Langmuir-Freundlich isotherm models. The α-Al₂O₃ support had a little adsorption capacity compared to the unsupport which had relatively larger adsorption capacity for CO₂ and CH₄. While the adsorption rates in the unsupport showed in the order of H₂> CO₂> N₂> CH₄ at low pressure range, the permeate flux in the membrane was in the order of H₂≫N₂> CH₄> CO₂. Separation properties of the unsupport could be confirmed by the separation experiments of adsorbable/non-adsorbable mixed gases, such as CO₂/H₂ and CH₄/H₂ systems. Although light and non-adsorbable molecules, such as H₂, showed the highest permeation in the single gas permeate experiments, heavier and strongly adsorbable molecules, such as CO₂ and CH₄, showed a higher separation factor (CO₂/H₂=5-7, CH₄/H₂=4-9). These results might be caused by the surface diffusion or/and blocking effects of adsorbed molecules in the unsupport. And these results could be explained by surface diffusion. This paper is dedicated to Professor Hyun-Ku Rhee on the occasion of his retirement from Seoul National University.