Dispersion of SiC in Aqueous Media with Al2O3 and Y2O3 as Sintering Additives |
| |
| Authors: | Jingxian Zhang Mikio Iwasa Dongliang Jiang |
| |
| Affiliation: | National Institute of Advanced Industrial Science and Technology, AIST Kansai, Osaka 563-8577, Japan; The State Key Laboratory of High Performance Ceramics and Superfine Structure, Shanghai Institute of Ceramics, Shanghai 200050, China |
| |
| Abstract: | It has been well accepted that polyethylene imine (PEI) is an effective dispersant for silicon carbide (SiC) in aqueous media. However, after the addition of sintering additives (Al2O3 and Y2O3), this dispersing effect is reduced significantly. In this work, a second dispersant, citric acid, was used to resolve this problem. It was found that citric acid could decrease the slurry viscosity (without sintering additives) and enhance the PEI adsorption on SiC particle surface. The optimal amount of citric acid required to achieve a minimum viscosity for 55 vol% SiC suspensions was equal to ∼0.87 wt% (at pH ∼6.8). With the aid of citric acid, well-stabilized SiC suspensions (containing sintering additives) were realized, which exhibited slight shear thinning rheologies. After tape casting and SPS sintering, dense SiC samples were obtained with a homogeneous fine-crystalline microstructure. Results showed that citric acid was an effective dispersant for improving the dispersion of SiC particles containing sintering additives. |
| |
| Keywords: | |
|
|