High cycle fatigue behaviour of Ti–6Al–4V alloy at elevated temperatures

High cycle fatigue behaviour of Ti–6Al–4V alloy was studied at 623 K and 723 K. Fatigue strength decreased at elevated temperatures compared with at ambient temperature. In the short life regime, fatigue strength was lower at 723 K than at 623 K, but in the long life regime it was nearly the same at both temperatures. At elevated temperatures, cracks were generated earlier at applied stresses below the fatigue limit at ambient temperature, indicating lowered crack initiation resistance. Small cracks grew faster at elevated temperatures than at ambient temperature, which became more noticeable with increasing temperature. After allowing for the elastic modulus, small cracks still grew faster at elevated temperatures.