Thermal Expansion Anisotropy and Acoustic Emission of NaZr2P3O12 Family Ceramics

Most members of the NaZr₂P₃O₁₂ (NZP) family possess low, near zero, overall thermal expansion coefficients. However, they also exhibit anisotropy of axial thermal expansion. Some compounds have opposite anisotropy; for example, the a parameter of CaZr₄P₆O₂₄ contracts on heating and that of SrZr₄P₆O₂₄ expands, while the c parameter expands for the Ca compound and contracts for the Sr compound. The anisotropy of the axial thermal expansion of these materials is believed to induce microcracking. The acoustic emission method was employed here to detect microcracking in ceramics due to the axial thermal expansion anisotropy. Acoustic signals were observed during cooling of the Ca and Sr compounds from 500°C, and Na and K compounds from 600°C. On the other hand, no acoustic emission signal is detected in Ca_0.5Sr_0.5Zr₄P₆O₂₄ ceramics, in which the lattice parameters a and c remain nearly unchanged in the temperature range of room temperature to 500°C. Thus, a direct correlation between microcracking of ceramics and their anisotropic axial thermal expansion coefficients was established by employing acoustic emission monitoring techniques.