Consolidation of Al2O3/Al Nanocomposite Powder by Cold Spray

While the improvement in mechanical properties of nanocomposites makes them attractive materials for structural applications, their processing still presents significant challenges. In this article, cold spray was used to consolidate milled Al and Al₂O₃/Al nanocomposite powders as well as the initial unmilled and unreinforced Al powder. The microstructure and nanohardness of the feedstock powders as well as those of the resulting coatings were compared. The results show that the large increase in hardness of the Al powder after mechanical milling is preserved after cold spraying. Good quality coating with low porosity is obtained from milled Al. However, the addition of Al₂O₃ to the Al powder during milling decreases the powder and coating nanohardness. This lower hardness is attributed to non-optimized milling parameters leading to cracked particles with insufficient Al₂O₃ embedding in Al. The coating produced from the milled Al₂O₃/Al mixture also showed lower particle cohesion and higher amount of porosity.