Sintering behavior and microwave dielectric properties of Bi2O3–ZnO–Nb2O5-based ceramics sintered under air and N2 atmosphere

The sintering behavior and dielectric properties of the monoclinic zirconolite-like structure compound Bi₂(Zn_1/3Nb_2/3)₂O₇ (BZN) and Bi₂(Zn_1/3Nb_2/3−xV_x)₂O₇ (BZNV, x = 0.001) sintered under air and N₂ atmosphere were investigated. The pure phase were obtained between 810 and 990 °C both for BZN and BZNV ceramics. The substitution of V₂O₅ and N₂ atmosphere accelerated the densification of ceramics slightly. The influences on microwave dielectric properties from different atmosphere were discussed in this work. The best microwave properties of BZN ceramics were obtained at 900 °C under N₂ atmosphere with _r = 76.1, Q = 850 and Q_f = 3260 GHz while the best properties of BZNV ceramics were got at 930 °C under air atmosphere with _r = 76.7, Q = 890 and Q_f = 3580 GHz. The temperature coefficient of resonant frequency τ_f was not obviously influenced by the different atmospheres. For BZN ceramics the τ_f was −79.8 ppm/°C while τ_f is −87.5 ppm/°C for BZNV ceramics.